水溶液中微波制备CdSe量子点问题
|
|
最近我们利用参考文献制备量子点，文献是8nm一下，可是我们做出来是200多纳米。资料是微波法合成，我用家用微波炉做了几次都达不到，请问你这个几纳米的怎么用微波做出来的？不用搅拌？通氮气么？谢谢！ 制备的文献操作见下面： Citrate-stabilized CdSe nanocrystals: Citrate-stabilized CdSe nanocrystals were prepared according to the following procedure: To 45 mL of water were added 0.05 g sodium citrate and 2 mL of 4*10-2 M cadmium perchlorate and the pH was adjusted to 9.0 by 0.1 M NaOH. The solution was bubbled with nitrogen for 10 min, 2 mL of 1*10-2 M N, N-dimethylselenourea was added, and the mixture was heated in a conventional 900 W (Sharp) microwave oven for 50 s. The final volume of the solution after heating was ca. 40 mL. In the recipe described above, the Cd:Se molar ratio was 4:1, which leads to CdSe nanoparticles with ca. 4.0 nm diameter; by increasing the Cd concentration it is possible to synthesize smaller CdSe nanocrystals.  |
回复此楼» 猜你喜欢
无机化学论文润色/翻译怎么收费?
已经有244人回复
» 本主题相关商家推荐: (我也要在这里推广)
» 本主题相关价值贴推荐，对您同样有帮助:
- CdSe量子点的定量问题。
已经有13人回复
- CdSe/ZnS量子点溶解性问题
已经有11人回复
- 请教一下QD-LED中CdSe量子点电致发光问题（激子单线态和三线态）
已经有3人回复
- 有没有不采用激光或者微波的方法来制备碳量子点的文献
已经有9人回复
- 有个关于量子点TEM表征的问题
已经有36人回复
- 【求助】一个没想清楚的问题—纳米粒子和量子点的区别
已经有21人回复
- 【求助】壳核结构的CdSe/ZnS量子点表面改性 荧光量子产率的问题
已经有12人回复
【答案】应助回帖
★
xjajx(金币+1): 鼓励有价值回复 2011-08-16 18:54:45
chemwen(金币+50): 5 2011-08-16 22:43:34
xjajx(金币+1): 鼓励有价值回复 2011-08-16 18:54:45
chemwen(金币+50): 5 2011-08-16 22:43:34
|
有专门的微波反应器卖，实验室以前买过一台，当时买几万块，现在几千可以买一台 顶部有个孔，可以通氮气，接机械搅拌，也可以磁力搅拌，同时功率，反应时间，反应液温度这些都可以自己设定 http://s.taobao.com/search?q=%CE ... mp;rt=1313428412298 |
2楼2011-08-16 01:21:06
3楼2011-08-16 01:32:57
chemwen
金虫 (正式写手)
- 应助: 0 (幼儿园)
- 金币: 2462.3
- 散金: 1
- 红花: 1
- 帖子: 513
- 在线: 183.1小时
- 虫号: 182378
- 注册: 2006-02-11
- 专业: 植物学研究的新技术、新方
4楼2011-08-16 07:59:20
40