Reaction sintering of lead zinc niobate-lead zirconate titanate ceramics
|
|||
|
Lead zinc niobate (PZN)-lead zirconate titanate (PZT) ceramics were produced by the reaction-sintering process. The specimens were prepared directly from a mixture of their constituent oxides without any calcination step. When 50% PZN was added to tetragonal Pb(Zr0.47Ti0.53)O3 ceramics, the densities and electrical properties were found to be optimal (ρ = 7.91 g/cm3, K = 1947 at 1 kHz and room temperature, d33 = 530 pC/N, kp = 0.61). However, the specimen containing more than 50% PZN showed reduced density and decreased electrical properties, due to the formation of pyrochlore phases. The improved densification behavior of the reaction-sintering process was attributed to the enhanced diffusion of lattice defects, which were created by differences in the ionic valence of the B-sites ions of the perovskite structure. © 2004 Elsevier Ltd. All rights reserved. (26 refs.) Journal of the European Ceramic Society, v 26, n 1-2, 2006, p 111-115 |
回复此楼» 猜你喜欢
科研求助
已经有3人回复
-
面上没中，邀请各位路过的虫友分析一下分数
已经有15人回复
-
博士去二本高校当辅导员，如何调整心态？
已经有10人回复
-
面上有专家说实验设备不是我们单位的
已经有6人回复
-
江苏省自然基金 什么时候出结果
已经有6人回复
-
广西大学-广州大学招聘博士后 欢迎广大优秀人才！！！
已经有11人回复
-
闲聊
已经有3人回复
-
两块石头
已经有10人回复
-
售SCI一区T0P文章，我:8O.55.1.O.54,科目全,可伽急
已经有15人回复
-
初秋的晨风
已经有6人回复