帮忙翻译下，谢谢
|
|
|
通过实验研究，可得以下结论： 1. β-环糊精（β-CD）作用下碳酸镧晶体的合成。制备出花状碳酸镧，颗粒大小约为10μm；制备出两端不同粗细的碳酸镧纳米管，管长约为2μm，管粗约为300~400nm。 2. 聚乙烯醇(PVA)作用下碳酸镧晶体的合成。制备出六棱片层碳酸镧，颗粒大小约为8μm；制备出碳酸镧纳米棒，棒长约为2μm，管粗约为300~400nm。 3. 以棉花为模板碳酸镧晶体的合成。制备出大小约为10μm的树状碳酸镧颗粒。 4. 通过钼锑抗法测定碳酸镧的磷结合效果。与磷结合能力最强的样品为聚乙烯醇作用下合成的碳酸镧纳米棒，此样品与磷酸盐溶液反应，达到反应终点所需时间最短，且终点溶液中磷含量最少。 |
回复此楼
wlfine82
木虫 (正式写手)
- 应助: 0 (幼儿园)
- 金币: 1023.8
- 红花: 1
- 帖子: 521
- 在线: 260.3小时
- 虫号: 706470
- 注册: 2009-02-23
- 专业: 污染控制化学
|
Through experimental research, the following conclusions can be drawn: 1. Synthesis of Lanthanum carbonate Crystals under the action of Β-cyclodextrin (β-CD) . Lanthanum carbonate prepared flower-like, particle size is about 10μm; prepared with different thickness of lanthanum carbonate at both ends of nanotubes, tube length is 2μm, Coarse about 300 ~ 400nm. 2. Polyvinyl alcohol (PVA) under the action of lanthanum carbonate Crystals. Preparation of a six-rowed lanthanum carbonate layers, particle size is about 8μm; prepared lanthanum carbonate nanorods, rod length is 2μm, Coarse about 300 ~ 400nm. 3. To cotton as the template synthesis of lanthanum carbonate crystals. Size of approximately 10μm was prepared tree lanthanum carbonate particles. 4. Through the determination of molybdenum antimony anti-P combined effects of lanthanum carbonate. The strongest binding with the phosphate sample as the synthesis of polyvinyl alcohol under the action of lanthanum carbonate nanorods, the reaction of the sample and the phosphate solution to achieve the shortest time the reaction end, and the phosphorus content of at least the end solution. |
2楼2010-05-09 15:27:57
xunmengzhang
木虫 (著名写手)
营长
- 应助: 2 (幼儿园)
- 金币: 6750.4
- 散金: 1268
- 红花: 9
- 帖子: 1619
- 在线: 294小时
- 虫号: 986070
- 注册: 2010-03-31
- 性别: GG
- 专业: 药物化学
|
Through experimental research, the availability of the following conclusions: 1. Β-cyclodextrin (β-CD) under the action of lanthanum carbonate Crystals. Lanthanum carbonate prepared flower-like, particle size is about 10μm; prepared with different thickness of lanthanum carbonate at both ends of nanotubes, tube length is 2μm, Coarse about 300 ~ 400nm. 2. Polyvinyl alcohol (PVA) under the action of lanthanum carbonate Crystals. Preparation of a six-rowed lanthanum carbonate layers, particle size is about 8μm; prepared lanthanum carbonate nanorods, rod length is 2μm, Coarse about 300 ~ 400nm. 3. To cotton as the template synthesis of lanthanum carbonate crystals. Size of approximately 10μm was prepared tree lanthanum carbonate particles. 4. Through the determination of molybdenum antimony anti-P combined effects of lanthanum carbonate. The strongest binding with the phosphate sample as the synthesis of polyvinyl alcohol under the action of lanthanum carbonate nanorods, the reaction of the sample and the phosphate solution to achieve the shortest time the reaction end, and the phosphorus content of at least the end solution. |
3楼2010-05-09 18:19:35
高兴星期五
铁杆木虫 (著名写手)
- 应助: 0 (幼儿园)
- 金币: 6875.5
- 散金: 73
- 帖子: 2240
- 在线: 28.4小时
- 虫号: 863010
- 注册: 2009-10-04
- 性别: MM
- 专业: 钢铁冶金
4楼2010-05-09 19:12:10
ss001
木虫 (著名写手)
财长就是财长
- 应助: 1 (幼儿园)
- 贵宾: 0.001
- 金币: 3913.2
- 红花: 2
- 沙发: 10
- 帖子: 2453
- 在线: 306.6小时
- 虫号: 844002
- 注册: 2009-09-09
- 专业: 等待。。。
5楼2010-05-09 22:36:10
|
In the study, one can obtain four conclusions. Crystalline lanthanum carbonate was synthesized with β-cyclodextrin(β-CD), shape as efflorescent, particle size about 10μm. The thickness of lanthanum Carbonate nanotubes is difference in both ends, longs about 2μm, diameters of 300-400μm. 看看行不？ |
6楼2010-05-10 09:36:39
高兴星期五(金币+160, 翻译EPI+1):非常感谢您 2010-05-10 09:59:33
|
Through experimental research, the following conclusions can be drawn: 1. Synthesis of carbonate Lanthanum Crystals under the action of Β-cyclodextrin (β-CD) . Flower-like carbonate Lanthanum has been prepared with the particle size of about 10μm; Besides, carbonate lanthanum nanotubes with different diameters at both ends have also been prepared with the tube length of about 2μm and diameters of about 300 ~ 400nm. 2. Synthesis of carbonate Lanthanum Crystals under the action of Polyvinyl alcohol (PVA). The six-rowed layered carbonate lanthanum crystals have been prepared with the particle size of about 8μm; Carbonate lanthanum nanorods have also prepared with the rod length of about 2μm and diameter of about 300 ~ 400nm. 3. Synthesis carbonate of lanthanum crystals based on the cotton template. Tree-like carbonate lanthanum particles with the size of about 10μm have been prepared. 4. The ability for carbonate lanthanum to combine with P was measured by anti-molybdenum (antimony) method. It found that the strongest binding with the phosphate sample was the carbonate lanthanum nanotubes synthesized under the action of polyvinyl alcohol. The reaction of the sample and the phosphate solution took the shortest time to the end, and the least phosphorus content remained in the end solution. |
7楼2010-05-10 09:51:20