| Mesoporous thick coatings have been prepared on commercially pure titanium substrate by microarc oxidation method in Al(OH)3 colloidal solution. By changing the pulse voltage amplitude, the effects of the voltage on the microstructure, phase composition and electrochromic properties of the coatings were investigated. The results show that the size of micropores existing on the coating surface gradually increase with increasing the voltage, meanwhile its pore density reduced. These thick porous coatings were completely consisted of rutile phase TiO2, and they are show good reversibility between blue coloration and bleaching cycles in pH 2.0 HCl solution. |
回复此楼» 猜你喜欢
萌生出自己或许不适合搞科研的想法，现在跑or等等看？
已经有3人回复
-
参与限项
已经有3人回复
-
假如你的研究生提出不合理要求
已经有7人回复
-
实验室接单子
已经有4人回复
-
全日制（定向）博士
已经有4人回复
-
对氯苯硼酸纯化
已经有3人回复
-
求助:我三月中下旬出站，青基依托单位怎么办？
已经有12人回复
-
所感
已经有4人回复
-
要不要辞职读博？
已经有7人回复
-
北核录用
已经有3人回复
3楼2009-12-30 09:15:02
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
zap65535(金币+15,VIP+0):补发 1-1 12:02
zap65535(金币+15,VIP+0):补发 1-1 12:02
| Mesoporous thick coatings have been prepared on commercially pure titanium substrate by microarc oxidation method in colloidal solution of Al(OH)3. By changing the pulse voltage amplitude, the effects of the voltage on the microstructure, phase composition and electro chromic properties of the coatings were investigated. The results show that the size of micropores existing on the coating surface gradually increases with the increasing of voltage. Meanwhile its pore density is reduced. These thick porous coatings are completely composed of rutile phase TiO2, and they show good reversibility between blue coloration and bleaching cycles in pH 2.0 HCl solution. |
2楼2009-12-30 09:14:38
4楼2009-12-30 09:19:38
goodtimega
铁杆木虫 (著名写手)
- 翻译EPI: 4
- 应助: 1 (幼儿园)
- 金币: 8138.7
- 散金: 570
- 红花: 1
- 帖子: 1489
- 在线: 527.5小时
- 虫号: 820248
- 注册: 2009-08-02
- 专业: 高分子材料结构与性能
| Mesoporous thick coatings have been prepared on commercially pure titanium substrate by microarc oxidation method in Al(OH)3 colloidal solution. By varying the amplitube of the pulse voltage, the effects of the voltage on the microstructure, phase composition, and electrochromic properties of the coatings were investigated. The results show that the size of micropores on the coating surface gradually increase with increasing the voltage, along with a reduction of the pore density. These thick porous coatings are completely conprised of rutile phase TiO2, and they show good reversibility between blue coloration and bleaching cycles in pH 2.0 HCl solution. |
5楼2009-12-30 09:21:39