[交流] 【求助】那位大牛能给解释下下面的图片的意思

看国外的论文，经常出现下面的图片，不知道什么意思，怎么才能作相似的研究呢？使用什么设备作的？

Evolution of the texture during cold rolling, φ2 = 45°, 65° and 90° sections of the ODF: (a) ε = 0, (b) ε = 0.05, (c) ε = 0.11, (d) ε = 0.22, (e) ε = 0.36, (f) ε = 0.51 (levels: 0.80, 1.00, 1.30, 1.60, 2.00, 2.50, 3.20, 4.00, 5.00).

这是论文针对这个图的原文
The evolution of the texture is shown by the ODF sections in Fig. 7. The cold-rolling strain increases from ε = 0 in Fig. 7a to ε = 0.51 in Fig. 7f. The hot-rolled texture (Fig. 7a) is very weak, with a maximum intensity of 2.0 times random for the cube component {0 0 1}1 0 0. The deformation textures are also relatively weak, with a maximum intensity of 5.0 times random for the sample with a rolling strain of ε = 0.51.

[ Last edited by wannerman on 2009-11-2 at 10:49 ]

回复此楼

» 猜你喜欢

飞飞飞

1楼 2009-11-02 10:42:35

已阅回复此楼关注TA 给TA发消息送TA红花 TA的回帖

sirljz

铁杆木虫 (著名写手)

Well spend every day！

应助: 0 (幼儿园)
贵宾: 0.282
金币: 6260.8
散金: 42
红花: 1
帖子: 1216
在线: 36.2小时
虫号: 614600
注册: 2008-09-28
性别: GG
专业: 金属结构材料

★ ★
小木虫(金币+0.5):给个红包，谢谢回帖交流
caocao4735(金币+1,VIP+0):回答verygood 呵呵 11-2 11:51

好像XRD就能够做到，这些图是分析织构的极图（或者反极图）吧，ODF是一种分析方法

赞一下(11人)

回复此楼

4楼2009-11-02 11:41:35

已阅回复此楼关注TA 给TA发消息送TA红花 TA的回帖

查看全部 14 个回答

xiaomuchong916

木虫 (著名写手)

应助: 1 (幼儿园)
金币: 6512
散金: 16
帖子: 1144
在线: 678.3小时
虫号: 553252
注册: 2008-05-02
专业: 金属功能材料

★ ★ ★
小木虫(金币+0.5):给个红包，谢谢回帖交流
deng1027(金币+2,VIP+0):谢谢耐心回复 11-2 18:10

从文字说明中看出这种图片好像是研究不同的ε及不同角度φ截面下的织构的发展过程。不知道对不对。

织构的测定方法：最准确、最方便的就是X光衍射法（在加工率比较大、晶粒不太粗大时较适用）。另外还有电子衍射法以及光学方法测织构。对于铁磁材料或者对称度很低的金属，也可以通过测定不同方向的磁学性质来测定织构。

楼主还可以看一下这个帖子http://muchong.com/bbs/viewthread.php?tid=1639614&fpage=1
里面有本讲织构材料三维取向分析（ODF）的书，应该有用。