小木虫论坛-学术科研互动平台» 学术交流区» 论文翻译 » 论文翻译求助完结子版 » 失重峰 用英语怎么说
北京石油化工学院2026年研究生招生接收调剂公告
51/1返回列表
查看: 405  |  回复: 5
只看楼主 @他人 存档 新回复提醒 (忽略) 收藏    在APP中查看
当前主题已经存档。
当前只显示满足指定条件的回帖，点击这里查看本话题的所有回帖

楼1970-01-01 08:00:00
已阅   申请翻译EPI   回复此楼   编辑   查看我的主页

slowstar

木虫 (职业作家)
Thermogravimetric Analysis. The TGA curves of the
OctTe(dO)-Au and OctS-Au NPs are compared in Figure 11.
A distinct two-step weight loss process was observed for the
OctTe(dO)-Au NPs (Figure 11a), which was significantly
different from the roughly one-step-like weight loss process
observed on the OctS-Au NPs (Figure 11b). The first weight
loss of ∼11.0% was observed in the temperature range from
∼100 to∼270 °C, and the second weight loss of∼11.2% occurred
between ∼605 and ∼800 °C. Shiny gold pieces were observed
only after the second weight loss. Thus, the first weight loss was
probably due to the destruction of the alkyl chains of ligands,
and the second was probably due to the remaining tellurium
oxide leaving the surface of Au NPs. In other words, the C-Te
bond was broken in the first step, and Te-Au bond breaking
occurred in the second step. In contrast, the OctS-AuNPs showed
a dominate weight loss (25%) from ∼100 to ∼220 °C, followed
by a small additional 3% weight loss that ended at∼500 °C. That
is, all ligands of OctS-Au NPs were gone before the temperature
reached 500 °C. After comparing the temperature of Te-Au
bond breaking with that of S-Au, it could be concluded that the
Te-Au NP bond is stronger than the S-Au bond.
赞一下 回复此楼
精韧不怠，日进有功
5楼2009-10-12 18:59:23
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
查看全部 6 个回答

slowstar

木虫 (职业作家)
★
复合钢管(金币+1,VIP+0): 10-12 18:17
weight loss peak
回复此楼
精韧不怠，日进有功
2楼2009-10-12 15:57:01
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

slowstar

木虫 (职业作家)
应该是weight loss ，加 peak 就多余了。
赞一下 回复此楼
精韧不怠，日进有功
4楼2009-10-12 18:57:03
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

slowstar

木虫 (职业作家)
★ ★ ★ ★ ★
复合钢管(金币+5,VIP+0): 10-13 10:10
to obtain the same weight loss rate,
relevant temperature increased with the enhancement of heating rates. When temperature was above 391.2℃ ，
thermogravimetric law was not impacted essentially by the heating rates with 20℃/min or higher, however, the
maximum weight loss took place when the heating rate was 10℃/min. Weight loss of wheat straw was not influenced
obviously by the Ni-catalyst. Thermogravimetric dynamic parameters of wheat straw were calculated without catalyst
and with 0.5% Ni-catalyst by the methods of Kissinger and Ozawa, respectively;
赞一下(1人) 回复此楼
精韧不怠，日进有功
6楼2009-10-12 19:01:15
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
查看全部 6 个回答
普通表情 龙 兔 虎 猫 高级回复 (可上传附件)
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[考研] 求调剂 +3 111623 2026-04-04 3/150 2026-04-05 01:35 by wxiongid
[考博] 申博 +7 IQwQl 2026-04-04 7/350 2026-04-04 23:32 by mumin1990
[考研] 292分，材料与化工，申请调剂 +22 程晴之 2026-04-01 26/1300 2026-04-04 22:03 by hemengdong
[考研] 085400电子信息319求调剂（接受跨专业调剂） +5 星星不眨眼喽 2026-04-03 6/300 2026-04-04 21:50 by hemengdong
[考研] 283求调剂 +4 mcbbc 2026-04-03 5/250 2026-04-04 20:51 by imissbao
[考研] 292求调剂 +11 2022080213 2026-04-04 13/650 2026-04-04 18:38 by macy2011
[考研] 考研生物学考A区211，初试322，科目生化和生物综合，求调剂 +4 。。。54 2026-04-03 4/200 2026-04-04 16:09 by dongzh2009
[考研] 一志愿C9的化学工程（085602） 340分，感觉校内调剂无望，求调剂 +9 万事宜臻 2026-04-04 9/450 2026-04-04 11:49 by 啵啵啵0119
[考研] 310求调剂 +18 争取九点睡 2026-03-30 18/900 2026-04-03 18:35 by ls刘帅
[考研] 285求调剂 +5 AZMK 2026-04-03 8/400 2026-04-03 18:17 by AZMK
[考研] 0856，269分求调剂 +15 有学上就行求求� 2026-03-30 18/900 2026-04-03 16:50 by melodiousnow
[考研] 289-求调剂 +4 这里是_ 2026-04-03 4/200 2026-04-03 14:23 by 1753564080
[考研] 一志愿a区211，085601-307分求调剂 +13 党嘉豪 2026-03-31 26/1300 2026-04-03 08:33 by 495374996
[考研] 085602化工求调剂（331分） +9 111@127 2026-03-30 9/450 2026-04-02 20:00 by dick_runner
[考研] 一志愿华南师范大学-22408计算机-292分-求华南师范大学调剂 +4 爱读书的小鳄鱼 2026-04-02 4/200 2026-04-02 18:35 by 求调剂zz
[考研] 一志愿郑大材料工程290求调剂 +20 Youth_ 2026-03-30 20/1000 2026-04-02 14:48 by 5896
[考研] 0832食品科学与工程学硕282调剂 +4 鱼在水中游a 2026-04-02 7/350 2026-04-02 14:12 by baoball
[考研] 初试301，代码085701环境工程，本硕一致，四六级已过，有二区一作，共发表5篇论文 +6 axibli 2026-04-01 6/300 2026-04-02 13:42 by Ecowxq666！
[考研] 环境工程调剂 +9 hyzzzzzzz. 2026-04-01 9/450 2026-04-01 14:20 by salamander`
[考研] 抱歉 +3 田洪有 2026-03-30 3/150 2026-03-30 19:11 by 迷糊CCPs
信息提示
关闭
请填处理意见
关闭