[求助]
不同直径介孔碳小球
|
||
急需 ！！有哪位大神在做，能请教一下么  赵东元院士课题组的 单分散高氮介孔碳纳米小球 不同直径的我这边重复的 没有做出小球来是怎么回事，是跟着如下这篇文献做的 Monodisperse Ultrahigh Nitrogen-Containing Mesoporous Carbon Nanospheres from Melamine-Formaldehyde Resin DingYi Guo ,ZhaoDongYuan The mesoporous MF polymer nanospheres were synthesized through a facile aqueous emulsion polymerization self-assembly process. Typically, 0.6 g of Pluronic F127 was dissolved in 10 mL of deionized water. Then 0.6 g of TMB was added and vigorously stirred for 6 h (denoted as solutionA). 3.0 mmol of melamine, 3.0 mmol of formaldehyde aqueous solution (37 wt%), and 0.05 mL of 0.1 m NaOH aqueous solution were added to 40 mL of deionized water and stirred at 100 °C for 0.5 h for the formation of soluble prepolymerized MF resin solution (denoted as solution B).Subsequently, the solution A was added into the above solution B and stirred for another 2 h to allow the formation of the stabilized TMB/F127 emulsion droplets. Afterward, appropriate amount of HCl aqueous solution, with a mole ratio of HCl to melamine in the range of 0.27–0.53, was added and continuously stirred over 6 h. Finally, the solution turned to bright milky white. The obtained mesoporous MF polymer nanospheres were collected by centrifugation and then washed with deionized water and absolute ethanol at least three times, respectively. After drying in an oven at 60 °C overnight, the white power was preheated at 350 °C for 3 h and finally calcined at 800 °C for 2 h in nitrogen atmosphere with a heating rate of 1 °C min−1to obtain the resultant ultrahigh nitrogen-containing mesoporous carbon nanospheres (N-MCSs). The products were denoted as MF-x and N-MCSs-x (where x represents the particle size in nanometers), respectively. 问题1：HCl是浓盐酸吗 里边没有表明所用浓度 问题2：当A溶液：F127溶液 +TMB 加入B溶液：三聚氰胺+甲醛（37%）+NaOH（0.1M） 是需要多少温度进行反应呢 我看其他文献一般是F127溶液加入后用的66或是70摄氏度 问题3：转速没有具体表明 ，只说是剧烈搅拌，我这边看文献有的说是500rpm 不知道有没有问题 问题4：有说表面活性剂是要针管慢慢注射的，我是直接一次性加入搅拌的 |
回复此楼» 猜你喜欢
化工学院（学院正式调剂群+联系方式）
已经有0人回复
-
化工学院（学院官方群）-院士团队招生-学生自由度高-培养模式成熟高效
已经有0人回复
-
无机化学论文润色/翻译怎么收费?
已经有191人回复
-
黑龙江大学分析化学招调剂
已经有0人回复
-
武汉高校国家级人才团队招收材料，化学，纺织等专业硕士调剂生
已经有26人回复
-
纺大化工学院（官方群）-院士团队招生-学生自由度高发展好-培养模式成熟
已经有0人回复
-
温州大学化材学院王娟课题组招生
已经有5人回复
-
学院官方群-院士团队招生-学生自由度高-培养模式成熟已有10余名学生赴985海外深造
已经有0人回复
-
武汉纺织大学化工学院官方群-院士团队招生-学生自由度高-10余名学生赴985海外深造
已经有0人回复
-
南昌航空大学蒋华麟教授课题组招收化学、环境、碳达峰碳中和及相关专业硕士信息
已经有0人回复
-
湖北师范大学复试调剂
已经有0人回复
» 本主题相关商家推荐: (我也要在这里推广)
2楼2022-05-11 16:28:46