1.The half-cells were assembled in an argon-filled glove box and galvanostatically charged and dischargedat a current density of 100 mA/g in the voltage range 0.02–1 V vs. Lit/Li.

2. The composite electrode was prepared by mixing 80 wt% Ba–Fe–Si/C powder, 5% acetylene black (AB) and 15% polytetrafluoroethylene into paste, then rolling the pasted mixture into ca. 0.1 mm thick electrode sheet (ca. 10 mg/cm2), and finally pressing the electrode sheet onto copper net.

3.The electrolyte was 1 M LiPF6 in a mixed solvent of ethylene carbonate (EC) and dimethyl carbonate (DMC) (1:1 by volume).

» 猜你喜欢

已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

longhua7085

至尊木虫 (著名写手)

★ ★
nandhutu(金币+2,VIP+0): 5-22 19:30
3.电解液为1 M LiPF6溶于碳酸乙烯酯(EC)和碳酸二甲酯(DMC)的混合溶剂(体积比1:1)中
2楼2009-05-22 16:10:00
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

963147963

金虫 (正式写手)

★ ★
nandhutu(金币+2,VIP+0): 5-22 19:30
1.半电池在氩气手套箱中组装,然后galvanostatically(galvano流电,电;statically静止的, 静态的; 静电的)充电,然后在0.02-0.1V范围内以100mA/g 的电流密度进行放电。
3楼2009-05-22 17:03:53
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

963147963

金虫 (正式写手)

★ ★
nandhutu(金币+2,VIP+0): 5-22 19:30
复合材料电极的制备过程是:混合80wt% (质量分数) 的Ba–Fe–Si/C 粉,5%乙炔黑和15%的聚四氟乙烯在糊剂中,把混合物轧制成0.1mm厚的电极薄板(ca. 10 mg/cm2), 最后把电极薄板压制到铜网上。
4楼2009-05-22 17:16:23
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
相关版块跳转 我要订阅楼主 nandhutu 的主题更新
普通表情 高级回复 (可上传附件)
最具人气热帖推荐 [查看全部] 作者 回/看 最后发表
[考研] 材料调剂 +4 爱擦汗的可乐冰 2026-02-28 4/200 2026-03-01 00:38 by 猫猫球alter
[基金申请] 面上模板改不了页边距吧? +5 ieewxg 2026-02-25 6/300 2026-03-01 00:10 by addressing
[考研] 307求调剂 +4 73372112 2026-02-28 6/300 2026-03-01 00:04 by ll247
[考研] 317一志愿华南理工电气工程求调剂 +5 Soliloquy_Q 2026-02-28 8/400 2026-02-28 23:36 by xyx2012xyx
[考研] 化工专硕348,一志愿985求调剂 +4 弗格个 2026-02-28 6/300 2026-02-28 22:00 by wang_dand
[考研] 290求调剂 +5 材料专硕调剂; 2026-02-28 6/300 2026-02-28 21:40 by gaoxiaoniuma
[考研] 295求调剂 +5 19171856320 2026-02-28 5/250 2026-02-28 21:39 by gaoxiaoniuma
[考博] 26申博 +4 想申博! 2026-02-26 4/200 2026-02-28 21:37 by limorning
[考研] 材料学调剂 +5 提神豆沙包 2026-02-28 5/250 2026-02-28 21:34 by gaoxiaoniuma
[考研] 264求调剂 +3 巴拉巴拉根556 2026-02-28 3/150 2026-02-28 21:31 by gaoxiaoniuma
[考研] 材料类求调剂 +6 wana_kiko 2026-02-28 6/300 2026-02-28 21:20 by gaoxiaoniuma
[考研] 求调剂 +4 repeatt?t 2026-02-28 4/200 2026-02-28 21:16 by gaoxiaoniuma
[考研] 284求调剂 +4 天下熯 2026-02-28 4/200 2026-02-28 21:13 by gaoxiaoniuma
[考研] 高分子化学与物理调剂 +4 好好好1233 2026-02-28 7/350 2026-02-28 20:42 by 好好好1233
[考研] 298求调剂 +8 人间唯你是清欢 2026-02-28 11/550 2026-02-28 20:26 by L135790
[考研] 276求调剂 +3 路lyh123 2026-02-28 4/200 2026-02-28 19:45 by 路lyh123
[考研] 0856调剂 +3 刘梦微 2026-02-28 3/150 2026-02-28 13:22 by houyaoxu
[硕博家园] 博士自荐 +6 科研狗111 2026-02-26 9/450 2026-02-28 12:32 by seaskyy
[考研] 298求调剂 +4 axyz3 2026-02-28 4/200 2026-02-28 11:21 by wang_dand
[基金申请] 面上可以超过30页吧? +12 阿拉贡aragon 2026-02-22 13/650 2026-02-26 22:09 by Hahaxia
信息提示
请填处理意见