[交流] 【求助】求助高温化学焊接技术

哪位朋友有介绍两种不同钢材(如碳钢和不锈钢)化学焊接技术制成复合材料的资料,提供一下.

[ Last edited by FLY_Phoenix on 2009-5-7 at 13:58 ]

回复此楼

» 猜你喜欢

» 本主题相关商家推荐: (我也要在这里推广)

1楼 2009-04-28 08:00:09

已阅回复此楼关注TA 给TA发消息送TA红花 TA的回帖

hui_jun_li

木虫 (正式写手)

MM-EPI: 3
应助: 0 (幼儿园)
贵宾: 0.07
金币: 1576.2
红花: 6
帖子: 514
在线: 22.1小时
虫号: 748650
注册: 2009-04-14
性别: GG
专业: 金属材料, 电镜

★ ★ ★ ★ ★
化学公社(金币+3,VIP+0): 4-30 07:34
ziice(金币+2,VIP+0):感谢您的交流，五一快乐 5-1 21:47

I think you are referring "thermit reaction welding"
An example as follows (using Al):
Thermit reaction details Aluminium reacts with iron oxides, particularly ferric oxide, in highly exothermic reactions, reducing the iron oxides to free iron, and forming a slag of aluminium oxide.

3Fe3O4+ 8Al = 4Al2O3+ 9Fe (3088°C, 719.3kCal↑)

3FeO + 2Al ⇒ Al2O3 + 3Fe (2500°C, 187.1kCal↑)

Fe2O3 + 2Al ⇒ Al2O3 + 2Fe (2960°C, 181.5kCal↑)

The various iron oxides are used in appropriate proportions so as to get the correct resultant quantity and temperature of molten steel. Approximately equal quantities of molten steel and liquid aluminium oxide are separated at about 2400°C, after a few seconds of the exothermic reaction. The iron obtained from such a reaction is soft and unusable as a weld metal for joining rails. To produce an alloy of the correct composition, alloys like ferro-manganese are added to the mixture along with pieces of mild steel, both as small particles, to allow rapid dissolution in the molten iron, to control the temperature and to increase the 'metal recovery'. Complete slag separation in a short time and better fluidity of the molten metal is achieved by adding compounds like calcium carbonate and fluorspar, etc.

Pre-heating the rail ends (to about 1000°C) is required to help the poured molten metal in washing away the surface oxidation on the rail ends, as otherwise, the molten metal may chill and solidify immediately on coming in contact with cold rail ends, without washing off the surface oxidation.

The procedure of 'controlled localized reaction' to keep the thermit mixture ignition under control was invented by Dr Goldschmidt and hence the process is sometimes also known as the Goldschmidt process. Individually patented processes have led to different trade names such as 'Thermit', 'Boutte', 'Argothem', etc.