[求助]
外扩散
|
|
书上外扩散的排除：在研究温度区间的最高温下，保证W/F空速不变，增加F则可以减小界面层的厚度，减小到足够小时则外扩散可忽略，表现出转化率不再增加。 那么对于下面来自一篇文献中的这段英文，对于外扩散的排除与上面书中方法有何异同，载气在其中扮演怎样的一个角色，难道这样也起到减小界面层厚度的作用？ In the kinetically controlled reaction regime, the conversion of the reactant should not depend on the total gas flow rate for a fixed value of the W/F ratio. This effect was experimentally studied at 500 ℃ using a steam/carbon ratio of 3 and a catalyst weight of 0.1 g. It was found that there was practically no change in the glycerol conversion (50%), while varying the N2 flow rate from 50 to 200 cm3 /min, and hence, the total volumetric flow rate (Q0 ) from 1095 to 1245 cm 3 /min at a W/FAO ratio equal to 0.4 g h/mol. Thus, it was established that the external mass transfer resistance was absent over the entire temperature range studied. 自己的实验：固定催化剂用量100mg，以及进料速度，只改变载气的速度，发现随着载气速度的增加，转化率是减小趋势，载气速度越大感觉转化率就不怎么减小了；到后面甚至感觉：在高的载气流速下，实验的重现性很差 ；催化剂的稳定性还没有载气流速很小的时候稳定（大气压下，载气分压达到96千帕，反应物分压只有几千帕。）。所以很想知道载气在反应系统中都会产生哪些作用？ 非常感谢。 |
回复此楼» 猜你喜欢
关于合成MIL-125的求助
已经有0人回复
-
双非本硕光催化方向想读博，请各位老师看看我！
已经有2人回复
-
专业论文润色/翻译怎么收费?
已经有243人回复
-
瑞典林雪平大学范立洲课题组现招聘博士后、岗位制博士生
已经有0人回复
-
中国科大仿生界面材料科学全国重点实验室戴懿涛研究员/江雷院士团队招聘科研助理
已经有0人回复
-
中国科大仿生界面材料科学全国重点实验室戴懿涛研究员/江雷院士团队招聘科研助理
已经有0人回复
-
寻求物理化学学报最新的投稿模板！
已经有4人回复
-
东南大学杰青/海优团队招聘催化方向博士后
已经有866人回复
-
投稿咨询
已经有7人回复
-
自科面上 散金币 祈福
已经有61人回复
-
铁钼催化剂成型
已经有2人回复
2楼2017-05-31 13:27:48
20