| 查看: 3260 | 回复: 3 | |||
xyhe88木虫 (正式写手)
|
[求助]
关于超级电容器材料CV曲线中随着扫速增加氧化峰偏移及消失的问题 已有2人参与
|
|
最近一篇文章大修，审稿人的提问，NiCo2O4/PPy-12电极材料在扫速20mV s-1下有明显氧化峰，但是作为对比的材料NiCo2O4/PPy-6和 NiCo2O4/PPy-24在扫速20mV s-1曲线形状扭曲，而且没有明显的氧化还原峰，审稿人认为随着PPy负载量的增加，CV曲线的变化没有规律。如何给出合理的解释？感谢大家！ In Fig. 6, the CV curve of NiCo2O4/PPy-12 sample at a scan rate of 20 mV s-1 show obvious oxidation and reduction peaks. In Fig. S2, the CV curves of both NiCo2O4/PPy-6 and NiCo2O4/PPy-24 samples at scan rate of 20 mV s-1 show distorted shape and no obvious oxidation peaks can be seen. Are there any mistake? If there is no mistake, it means that with the increase of PPy on NiCo2O4, the change of CV curves is irregular. Please give an explanation.  Fig. 6 NiCo2O4/PPy-12 at a scan rate of 20 mV s-1  Fig. S2, the CV curves of both NiCo2O4/PPy-6 and NiCo2O4/PPy-24 at a scan rate of 20 mV s-1 |
回复此楼» 收录本帖的淘帖专辑推荐
 电化学方面的 |
» 猜你喜欢
CSC & MSCA 博洛尼亚大学能源材料课题组博士/博士后招生｜MSCA经费充足、排名优
已经有6人回复
-
德国Karlsruhe Institute of Technology招收电化学储能及联合培养CSC博士等
已经有20人回复
-
分析化学论文润色/翻译怎么收费?
已经有162人回复
-
德国Karlsruhe Institute of Technology招收电化学储能及联合培养CSC博士
已经有24人回复
-
德国Karlsruhe Institute of Technology招收电化学储能及联合培养CSC博士
已经有1人回复
-
固态锂金属电池迁移数计算求助
已经有1人回复
-
荷兰奈梅亨大学赵文博与Galimberti课题组招收理论计算CSC博士 2000 欧元/月+房补
已经有0人回复
-
26储能博士申请自荐
已经有22人回复
-
上海交通大学--宁波东方理工大学电池方向博士招生
已经有10人回复
-
海南大学全国重点实验室杨金霖老师招收储能电池方向博士生（2026年3月报名，9月入学）
已经有0人回复
-
海南师范大学2026年博士研究生招收 (在职想提升学历人员可报考) 申请考核制+普通招考
已经有0人回复
» 本主题相关商家推荐: (我也要在这里推广)
天闲星君
至尊木虫 (著名写手)
- 应助: 71 (初中生)
- 金币: 21234.6
- 红花: 12
- 帖子: 1996
- 在线: 916.9小时
- 虫号: 1125560
- 注册: 2010-10-18
- 专业: 电化学
2楼2017-04-17 18:41:38
【答案】应助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★
感谢参与，应助指数 +1
xyhe88: 金币+10, ★有帮助 2017-04-19 19:42:34
感谢参与，应助指数 +1
xyhe88: 金币+10, ★有帮助 2017-04-19 19:42:34
|
ppy是什么 对你这个不太懂，应该是ppy这种物质的量从6，变化为12又变化为24，如果量是递增的，你这里认为12好，那么6和24确实无规律，因为6和24都抑制了氧化还原反应，而只有12比他们抑制得少，可以比较峰电流的大小得出 发自小木虫Android客户端 |