[求助]
请教两个问题，用VASP算二维材料异质结的光吸收谱和能带出现问题，不胜感激 已有1人参与
|
|
请教两个问题哈。 其一：用VASP算二维材料异质结的光吸收谱，画图出现了多条线，请问大概是什么问题呀？ INCAR设置如下： LHFCALC = .TRUE. HFSCREEN = 0.2 ISTART = 1 ICHARG = 2 ISMEAR = -5 SIGMA = 0.05 NSW = 0 IBRION = -1 #ISIF = 2 EDIFF = 0.00001 #EDIFFG = -0.02 ENCUT=550 LREAL = FALSE ALGO = Damped TIME = 0.2 PRECFOCK = Fast LORBIT = 10 LWAVE = FALSE LCHARG = FALSE ADDGRID = FALSE. LHYPERFINE = FALSE. NEDOS = 20000 NELM = 200 LOPTICS = .TRUE. CSHIFT = 0.1 其二：用VASP算二维材料异质结的能带，画图出现能带交叉很乱…… INCAR设置如下： ISTART = 1 ICHARG = 2 ISMEAR = 0 SIGMA = 0.1 NSW = 0 IBRION = -1 #ISIF = 2 EDIFF = 0.00001 #EDIFFG = -0.02 ENCUT=550 LREAL= F ICORELEVEL = 1 #HSE LHFCALC = .TRUE. HFSCREEN = 0.2 ALGO = Damped TIME = 0.4 PRECFOCK = Fast AEXX = 0.25 #output IVDW=11 LORBIT = 10 LWAVE = .TRUE. LCHARG = .TRUE. LAECHG = T LVTOT = T NEDOS = 2000  光学吸收谱.png  能带图.png |
回复此楼» 猜你喜欢
情人节自我反思：在爱情中有过遗憾吗？
已经有6人回复
-
基金正文30页指的是报告正文还是整个申请书
已经有4人回复
-
今年春晚有几个节目很不错，点赞！
已经有6人回复
-
球磨粉体时遇到了大的问题，请指教！
已经有15人回复
-
过年走亲戚时感受到了所开私家车的鄙视链
已经有5人回复
-
江汉大学解明教授课题组招博士研究生/博士后
已经有3人回复
» 本主题相关商家推荐: (我也要在这里推广)
» 本主题相关价值贴推荐，对您同样有帮助:
- 有用过DSC的么，有问题请教。
已经有4人回复
2楼2017-03-14 10:18:19
3楼2017-03-18 16:47:37
4楼2017-03-19 16:07:19
|
您好 我算两层WS2时，结构优化得到的层间距特别大，相应的原来设置的真空层变小了，导致能带结构有误，请问结构优化的incar可以给我看看吗 能带结构乱可能是因为超胞有什么band folding 啥的 我不太清楚但是见过 发自小木虫IOS客户端 |
5楼2017-04-03 13:13:57
6楼2017-04-05 23:36:23
7楼2018-05-11 21:24:00
8楼2018-06-20 09:48:05