修饰电极基础问题，请教！急哦！
|
|||
|
我们现在想把碳纳米管修饰到玻碳电极表面上，原文如下：The glassy carbon(GC) electrode (Φ= 4 mm) was polished with 1.0, 0.3 and 0.05um alumina slurry, respectively, and then ultrasonically cleaned in ethanol and water. In 10mL of 0.2 wt% SDS aqueous solution, 10 mg of the acid-treated MWNT was ultrasonically dispersed to give a black suspension of 1.0 mg/mL. Subsequently, 20 ul of this black suspension was cast on a cleaned GC electrode surface. 但没有参考文献，不知道具体的处理方法，尤其是如何将碳纳米管酸处理，有没有哪位师兄师姐做过，请指教一下啊。 [ Last edited by Rainycc on 2009-2-27 at 10:06 ] |
回复此楼» 猜你喜欢
锂离子电池循环寿命衰减过快，求机理分析与改进思路
已经有2人回复
-
求博导收留
已经有6人回复
-
物理化学论文润色/翻译怎么收费?
已经有83人回复
-
CSC & MSCA 博洛尼亚大学能源材料课题组博士/博士后招生｜MSCA经费充足、排名优
已经有6人回复
-
德国Karlsruhe Institute of Technology招收电化学储能及联合培养CSC博士等
已经有20人回复
-
德国Karlsruhe Institute of Technology招收电化学储能及联合培养CSC博士
已经有23人回复
-
德国Karlsruhe Institute of Technology招收电化学储能及联合培养CSC博士
已经有1人回复
-
固态锂金属电池迁移数计算求助
已经有1人回复
-
荷兰奈梅亨大学赵文博与Galimberti课题组招收理论计算CSC博士 2000 欧元/月+房补
已经有0人回复
-
26储能博士申请自荐
已经有22人回复
-
上海交通大学--宁波东方理工大学电池方向博士招生
已经有10人回复
» 本主题相关商家推荐: (我也要在这里推广)
qyvec
木虫 (小有名气)
- 应助: 0 (幼儿园)
- 金币: 6842.8
- 散金: 8
- 帖子: 137
- 在线: 295.5小时
- 虫号: 463065
- 注册: 2007-11-19
- 专业: 其他无机非金属材料
★
wncpp(金币+1,VIP+0): 4-23 13:17
wncpp(金币+1,VIP+0): 4-23 13:17
|
The synthesized MWCNTs were purified by refluxing them with 60% HNO3 at 90 ◦C for 2 h. Then, the mixturewas diluted withwater, filtered, washed with excess de-ionized (DI) water and dried at 50 ◦C in a vacuum oven for overnight. After the purification process, the surface oxidation of the MWCNTs was carried out by refluxingMWCNTsin 4MH2SO4 +4MHNO3 at 90 ◦C for 5 h. Finally, the treated MWCNTs were diluted with water, filtered, washed with excess DI water, and dried at 50 ◦C in a vacuum oven for overnight. 文献中基本上就是硝酸这样去处理的，不过没有做过！ |
2楼2008-12-15 15:31:55
3楼2008-12-15 16:45:48
4楼2008-12-16 14:50:01
sunblog2008
木虫 (正式写手)
- 应助: 0 (幼儿园)
- 金币: 2094.1
- 散金: 92
- 红花: 2
- 帖子: 748
- 在线: 44.5小时
- 虫号: 320270
- 注册: 2007-03-10
- 性别: GG
- 专业: 光学
★
wncpp(金币+1,VIP+0): 4-23 13:17
wncpp(金币+1,VIP+0): 4-23 13:17
| The synthesized MWCNTs were purified by refluxing them with 60% HNO3 at 90 ◦C for 2 h. Then, the mixturewas diluted withwater, filtered, washed with excess de-ionized (DI) water and dried at 50 ◦C in a vacuum oven for overnight. After the purification process,the surface oxidation of the MWCNTs was carried out by refluxingMWCNTsin 4MH2SO4 +4MHNO3 at 90 ◦C for 5 h.Finally, the treated MWCNTs were diluted with water, filtered,washed with excess DI water, and dried at 50 ◦C in a vacuum oven for overnight |
5楼2008-12-17 08:41:18