塑料薄膜的拉伸模量
|
|
In this study the tensile stress/strain behavior of various consumer plastic thin film materials was measured using a low mass mechanical analyzer. Film thicknesses varied from 19 mm to 66 mm (0.75 mil to 2.6 mil). In this study the force applied to the samples was ramped at 0.05 N/min from 0.05 N to 1 N and sample strain was followed. All measurements were made at ambient conditions. The tensile behavior of the consumer products were compared qualitatively and quantitatively. Three mechanical phenomena were observed in the materials: linear elastic behavior, a strengthening or increase in modulus, and yielding or rapid elongation with minimal changes in stress. In the linear elastic region modulus was measured as defined by the inverse of the slope of the stress versus strain curve. Modulus values of 87 MPa to 6 GPa were observed. |
回复此楼» 本帖附件资源列表
-
欢迎监督和反馈：小木虫仅提供交流平台，不对该内容负责。
本内容由用户自主发布，如果其内容涉及到知识产权问题，其责任在于用户本人，如对版权有异议，请联系邮箱：xiaomuchong@tal.com - 附件 1 : TA038.PDF
2016-06-30 15:04:43, 791.07 K
» 猜你喜欢
今年E04面上
已经有17人回复
-
2026年面上项目中了，2A+B, 会评顺利通过
已经有10人回复
-
大龄残疾硕士的一点执念
已经有16人回复
-
刑法学论文投稿求助
已经有5人回复
-
Journal of Environmental Chemical Engineering
已经有3人回复
-
最后一年，祈求好运
已经有3人回复
-
风电环氧领域
已经有3人回复
-
售T0P一区SCI文章，我:8O5.51.O.54,科目齐全,可＋急
已经有4人回复
-
植酸TLC薄层色谱爬板
已经有6人回复