塑料薄膜的拉伸模量测量
|
|
In this study the tensile stress/strain behavior of various consumer plastic thin film materials was measured using a low mass mechanical analyzer. Film thicknesses varied from 19 mm to 66 mm (0.75 mil to 2.6 mil). In this study the force applied to the samples was ramped at 0.05 N/min from 0.05 N to 1 N and sample strain was followed. All measurements were made at ambient conditions. The tensile behavior of the consumer products were compared qualitatively and quantitatively. Three mechanical phenomena were observed in the materials: linear elastic behavior, a strengthening or increase in modulus, and yielding or rapid elongation with minimal changes in stress. In the linear elastic region modulus was measured as defined by the inverse of the slope of the stress versus strain curve. Modulus values of 87 MPa to 6 GPa were observed. |
回复此楼» 本帖附件资源列表
-
欢迎监督和反馈：小木虫仅提供交流平台，不对该内容负责。
本内容由用户自主发布，如果其内容涉及到知识产权问题，其责任在于用户本人，如对版权有异议，请联系邮箱：xiaomuchong@tal.com - 附件 1 : 塑料薄膜的拉伸模量.PDF
2016-03-30 09:11:41, 791.07 K
» 猜你喜欢
一志愿985，本科211，0817化学工程与技术319求调剂
已经有10人回复
-
一志愿吉林大学材料学硕321求调剂
已经有8人回复
-
一志愿中海洋材料工程专硕330分求调剂
已经有6人回复
-
一志愿西安交通大学材料工程专业 282分求调剂
已经有3人回复
-
332求调剂
已经有3人回复
-
294求调剂材料与化工专硕
已经有7人回复
-
281求调剂（0805）
已经有17人回复
-
267一志愿南京工业大学0817化工求调剂
已经有10人回复
-
0817调剂
已经有3人回复
-
焦虑
已经有13人回复