[交流] 斯坦福Cui Yi在NATURE NANOTECHNOLOGY再发新文：锂金属负极材料已有5人参与

Title：Interconnected hollow carbon nanospheres for stable lithium metal anodes
Abstract：For future applications in portable electronics, electric vehicles and grid storage, batteries with higher energy storage
density than existing lithium ion batteries need to be developed. Recent efforts in this direction have focused on highcapacity electrode materials such as lithium metal, silicon and tin as anodes, and sulphur and oxygen as cathodes. Lithium metal would be the optimal choice as an anode material, because it has the highest specific capacity (3,860 mAh g–1) and the lowest anode potential of all. However, the lithium anode forms dendritic and mossy metal deposits, leading to serious safety concerns and low Coulombic efficiency during charge/discharge cycles. Although advanced characterization techniques have helped shed light on the lithium growth process, effective strategies to improve lithium metal anode cycling remain elusive. Here, we show that coating the lithium metal anode with a monolayer of interconnected amorphous hollow carbon nanospheres helps isolate the lithium metal depositions and facilitates the formation of a stable solid electrolyte interphase. We show that lithium dendrites do not form up to a practical current density of 1 mA cm–2 .TheCoulombic efficiency improves to～99% for more than 150 cycles. This is significantly better than the bare unmodified samples, which usually show rapid Coulombic efficiency decay in fewer than 100 cycles. Our results indicate that nanoscale interfacial engineering could be a promising strategy to tackle the intrinsic problems of lithium metal anodes.

斯坦福Cui Yi在NATURE NANOTECHNOLOGY再发新文：锂金属负极材料-1

回复此楼