[求助] SOFC阴极测试两电极和三电极有何区别？

SOFC阴极测试两电极和三电极有何区别？
审稿人提的意见，不知道怎样才能回答的准确。
The authors use an asymmetric cell with porous Pt (from paste) as counter electrode. The reference electrode is a Pt wire placed on the side of the working electrode. There has been significant debate in literature on the problems with this setup. The authors should provide a drawing of the actual cell arrangement and provide evidence that this geometry does not suffer from imbalance between reference and working electrode. That is the ASR for the Pt electrode should be significantly smaller than the ASR of the  electrode. It would have been better when part of the study (under zero bias) was done in a symmetrical cell.
希望高人写出怎样回答，示意图意见画完，只是回答后面的问题就行，回答不错的话，追加50币。谢谢
回复此楼

» 猜你喜欢

» 本主题相关价值贴推荐，对您同样有帮助:
1楼 2013-08-24 15:45:14
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

titant

金虫 (正式写手)
感谢上面朋友回答，我用的是三电极法测试的
赞一下 回复此楼
4楼2013-08-26 14:56:42
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖
查看全部 5 个回答

cxguo

新虫 (正式写手)
你好，我不清楚你具体是怎么测试的。审稿人的意思是没有人用你这种方法来测试的。你测阴极极化电阻为什么不用对称电池测试（电解质两侧都是你的阴极not porous Pt）呢？
赞一下(1人) 回复此楼
2楼2013-08-26 06:42:44
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

cxguo

新虫 (正式写手)
你测出来的ASR包括了Pt 对电极的极化电阻，如果要用你这种方法测，必须证明明Pt电极的极化电阻要比你阴极的极化电阻要小很多
赞一下(1人) 回复此楼
3楼2013-08-26 06:46:44
已阅   回复此楼   关注TA 给TA发消息 送TA红花 TA的回帖

keaneding

木虫 (小有名气)

【答案】应助回帖

不知道你是怎么测试的，如果只是测试OCV条件下的Rp，reviewer说的不错，对称电池就足够了，而且数据非常reliable。对于三电极测试，一般是用在加偏压（bias）测试，目的是为了排除对电极在极化条件下对最后获得的阻抗谱的影响。在固体电化学的三电极测试中，参比电极的放置对最后的测试结果影响很大。正如reviewer所说，这在文献里面有很多讨论也有很多争议。我想你最好提供一组对称电池的测试结果。这个应该比三电极制备容易得多。
赞一下 回复此楼
5楼2013-09-20 06:11:28