[求助]
紧急求助：关于腐蚀的一篇论文，我没看懂审稿人想要问什么问题
|
|
虽然是和论文有关的，但请版主高抬贵手，因为我想在专业论坛里获得更专业的解决。多谢！ 文章要大修，但审稿人提的几个修改意见我硬是没看懂他要问什么？ 问题：Page 5, line 4. You must include the pH solution at all temperatures in order to obtain a better analysis of the corrosion results.在这部分我的原文是： Generally, with the increasing of temperature the solubility of H2S and/or CO2 in the water decreases. So there are comparatively more H2S and CO2 dissolved in the solution at 90°C, which results in the pH at 90°C is lower than that at other temperatures and the dissolution of anodic ** steel is accelerated。（试验条件一共90°C、110°C、130°C、150°C四个温度点。我的意思是温度越高，溶入水的H2S and/or CO2 就越少，PH值就越高。所以在四个温度中，90°C温度最低，PH值就最小，因此能加速**钢的腐蚀。） 他想让我干什么？ |
回复此楼» 猜你喜欢
Renlab@monash全奖博士机会，最后三天！
已经有0人回复
-
今年面上没有消息，想来是没了，散个金攒攒人品，为明年祈福
已经有698人回复
-
物理化学论文润色/翻译怎么收费?
已经有287人回复
-
合肥工业大学854仪器技术综合专业课考研
已经有0人回复
-
27年电化学博士毕业，想找海外QS前50的高校读博后求推荐
已经有3人回复
-
27年电池/材料类博士申请
已经有2人回复
-
2027年博士申请或转博科研助理 求推荐
已经有1人回复
-
请问谁有2025最新影响因子Excel表？金币求助！
已经有53人回复
-
氯化钠与有机磺酸分离
已经有1人回复
-
瑞典-博后-固态电池-粘结剂-锂离子电池方向
已经有53人回复
» 本主题相关价值贴推荐，对您同样有帮助:
- 急求，关于推荐审稿人的写法，有图有问题
已经有5人回复
- 求助！文章审稿意见回来，审稿人的问题我不明白，求高人指点！
已经有4人回复
- 【求助】小弟ATK计算的文章，求助审稿人关于能带的一个问题！江湖告急！ 望大家多帮忙
已经有9人回复
- 急急急！！！求助各位虫友，如何回答审稿人补充实验的问题
已经有28人回复
- 请教sci高手审稿人问题，急！
已经有22人回复
- 加个新问题 ACS applied materials & interfaces 达审稿人意见求助
已经有13人回复
- Journal of Materials Science: Materials in Electronics 推荐审稿人，紧急求助
已经有11人回复
- 【求助】紧急求助！审稿人问关于N2吸脱附表征的问题，这该怎么解释啊？？？？
已经有5人回复
- 请问各位大侠，审稿人是想说我统计部分出什么问题了？
已经有11人回复
- 求助 Materials letters -回复审稿人的问题
已经有4人回复
- 我的回答审稿人问题的文书例子
已经有79人回复
2楼2011-11-27 20:35:32
3楼2011-11-28 20:23:32
4楼2011-11-28 21:20:41
SCE_bar
新虫 (正式写手)
- ECEPI: 12
- 应助: 160 (高中生)
- 金币: 3276.6
- 散金: 80
- 红花: 12
- 帖子: 522
- 在线: 212.5小时
- 虫号: 1464390
- 注册: 2011-10-27
- 专业: 电化学
【答案】应助回帖
fuid(金币+3): 多谢，剩下能发放的金币不多了 2011-11-29 20:26:58
|
You can analyze the corrosion process of steel in H2S/CO2 solution with some literature reports. What influences the corrosion process of steel in H2S/CO2 solution? temperature, pH, solubility of H2S/CO2, film on steel and so on. You will get some reports/publication about the influence of pH, influence of temperature on the solubility of H2S/CO2, then explain a possible conclusion from literature report for your defense. Professor Srdjan Nesic at Ohio university (the Institute for Corrosion and Multiphase Technology) is No #1 in corrosion of oil and gas industry , they also use lots of GAMRY instruments for their researches there. http://www.corrosioncenter.ohiou.edu/projects/ you can find more reports from their publications in order to explain your results. |
5楼2011-11-29 05:09:58
tommy7749
至尊木虫 (职业作家)
- ECEPI: 1
- 应助: 27 (小学生)
- 金币: 31326.7
- 红花: 10
- 帖子: 3232
- 在线: 225.3小时
- 虫号: 513390
- 注册: 2008-02-27
- 专业: 电化学
【答案】应助回帖
fuid(金币+2): 多谢，剩下能发放的金币不多了 2011-11-29 20:27:06
|
1.“气体溶解度随温度升高而降低”只是一般情况下（比如，常温、常压，气体和溶液不会发生反应）。但是你的实验是在“高压反应釜”中进行，这个时候的溶解度就未必遵循这个规律（H2S和CO2是否会和溶液中某些物质反应？）。另外，溶解度大，PH在这种情况下也未必就小。因为PH是溶液中的H+浓度，而H+是气体和水反应生成的酸电离的结果。在你实验的情况下，（不知道是否高温），电离系数是否受到影响？所以，审稿人是有理由怀疑你凭“常理”推断出的结论的。 2.SCE的建议好！如果实在无法测试，只能引用文献(即使这个文献的结论有争议)导出有利于自己的结论。 |
6楼2011-11-29 14:10:06