【求助】电沉积纳米金

作者 taohanhan1
来源: 小木虫 700 14 举报帖子
+关注

请问电化学沉积纳米金时在-0.2V电沉积400S应采用什么技术(the electrode was immersed in 0.2 M Na2SO4 solution containing 1 mM HAuCl4 。AuCl4 - adsorbed on the CNTs–CS film were changed into AuNPs with potentiostatic electrodeposition for 400s at -0.2 V.)? 返回小木虫查看更多

今日热帖
  • 精华评论
  • JoshuaYH

    应该就是用i-t曲线吧

    [ Last edited by JoshuaYH on 2010-12-17 at 23:19 ]

  • taohanhan1

    谢谢关注,i-v曲线?具体在电化学工作站采用那种技术获得呢?

  • JoshuaYH

    是i-t,抱歉刚才写错了,就是电流-时间

  • wu_yu

    就是即使电流法了 控制V恒定 测定I随t的变化

  • axz123.com

    引用回帖:
    Originally posted by taohanhan1 at 2010-12-17 22:08:29:
    请问电化学沉积纳米金时在-0.2V电沉积400S应采用什么技术(the electrode was immersed in 0.2 M Na2SO4 solution containing 1 mM HAuCl4 。AuCl4 - adsorbed on the CNTs–CS film were changed into AuNPs wit ...

    文献中就说,溶液为0.2M Na2SO4和1mMHAuCl4,工作站上 i-t 曲线设定电压为-0.2V,还原时间400s,估计还得自己调整!呵呵

    [ Last edited by axz123.com on 2010-12-20 at 14:37 ]

  • 胡琪

    it曲线是这样的用这个做的在5 mmol/L HAuCl4溶液中采用循环伏安法在-0.2~0.5V 范围内, 扫速为0.05mV/s 电沉积20 圈, 取出用二次蒸馏水洗去电极表面残留的HAuCl4溶液
    【求助】电沉积纳米金